Aluminium Alloy Magnesium Silicon 6082

  ALUMINUM ALLOY MAGNESIUM SILICON 6082

Products
Sheets - Plates - Bars Pipes, Profiles, Wire

Aplications and uses
Molds industry of the footwear.
Molds of bottles of plastic for blown.
Molds of thermoformed.
Molds industry of the rubber.
Molds and counterfoils for the industry in general.
Models for the smelting plates.

General use in construction and machinery and industrial vehicles.

Thermal treatments
Placed in solution: 535º C + - 5º C to 0,5 at 2 hours.
Placed in cold water (40º C max). The sooner the better.
Hardness: State T4, 8 days mínimum at 20º C.
Artificial hardness: State T6, 16 hours a 165º C + - 5º C or 8 hours at 175º C += 5º C.

Annealing: From 30 min. to 2 hours at 380º -420º C, Right after slow cooling .
Job is hot: From 300º to 490ºC.

Technological competence 

MB: very good
B: good
R: moderate
M: bad, avoid


Weld
- On the fire..............................(MB)
- To the low Arch gas argon..............(B)
- Under electrical resistance........(MB)
- Braised ...............................(B)


Mechanization:
-Fragmentation of the chip. State 0: (M) State: T6 (R)
-Surface sheen....................State0: (-) State : T6 (MB)

Natural Composure

-Under rural climate................(MB)
-Under industrial climate.........(MB)
-Under sea conditions.............(B)
-In salt water...... ..................(R)


Embuticíon:
-Expansion ................... State: 0 (MB) State: T6 (M)
-Stamping deep.......State:0 (MB) State: T6 (M)


Anodized
-Protection .........................(MB)
-Decorative ........................(R)
-Anodized last .................(MB)

Embossed
-State :0 ...........................(B)

 
Chemical composition
%
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
 
Other
Al
Min.Max
0,70
1,30
0,50
0,10
0,40
1,00
0,60
1,20
0,25
0,20
-
-
0,10
Rest
                       

International Equivalencies
USA
SPAIN
FRANCE
GERMANY
G.B
SWEEDEN
SWITZERLAND
CANADA
ITALY
A.A.
 
U.N.E.
AFNOR
DIN(1712-1725)
B.S.
S.I.S.
VSM
ALCAN
UNI
6082
 
L-3453
38.348
A-SG M0,7
AIMSi1
3.2315
H30
4212
AIMgSiMn
-
3571

Mechanical Properties
State
Burst load
Rm N/mm2
Elasticty Limit
Rp 0.2 N/mm2
Length
5,65 V So
Resistence to
Shear
N/mm2
Life Span
Brinell(HB)
Vickers
T4
215
130
15
178
70
74
76
305
270
8
218
100
105

Physical Properties
Elastic module
N/mm2
Specific gravity
gms/cm3
Temperature of fusion
ºC
Coefficient of
dilatac. linear
(20º-100º) 10-6/ºC
Thermal Conductivity
w/m ºC
Electrical Resistance
Micro Ohm cm.
Electrical Conductive-ness
% IACS
Potential to dilute
V.
69.500
2,70
570-660
23´5
184
3´7
48´6
0´83

Folding radii
State
Coef
0´4-0´8 m/m
0´8-1´6 m/m
1´6-3´2 m/m
3´2-4´8 m/m
4´8-6 m/m
6-10 m/m
10-12 m/m
0
K
0
0´5
1
1´5
1´75
2
2´5
T4
K
1
1´5
2
2´5
3
3´5
4
T6
K
2
2´5
3´5
4
4´5
5
6
 
 



 

Normalized measurements 1.050
Size
m/m
Thickness
m/m
Thickness
m/m
Size
m/m
1
1250 x 2500
35
1500 x 3000
1´5
1250 x 2500
40
1500 x 3000
2
1250 x 2500
45
1500 x 3000
2
1500 x 3000
50
1500 x 3000
2´5
1250 x 2500
60
1500 x 3000
3
1500 x 3000
70
1500 x 3000
4
1250 x 2500
80
1500 x 3000
4
1500 x 3000
90
1500 x 3000
5
1500 x 3000
100
1500 x 3000
6
1500 x 3000
110
1500 x 3000
8
1500 x 3000
120
1500 x 3000
10
1500 x 3000
130
1500 x 3000
12
1500 x 3000
140
1500 x 3000
15
1500 x 3000
150
1500 x 3000
20
1500 x 3000
180
1500 x 3000
25
1500 x 3000
200
1500 x 3000
30
1500 x 3000
   

Headquarters

VALENCIA Pol. Ind. Fuente del Jarro C/Ciudad de Elda, 17-19 46988, Paterna, Valencia broncesval@broncesval.com

Commercial Tel. 96 134 07 76
Fax. 96 134 09 43

Admin. Tel. 96 134 34 21
Fax.96 134 12 28

Delegations

CATALUNYA Pol. Ind. Molí dén Xec Can Barneda, 5  (Junto Baricentro), 08291, Ripollet catalunya@broncesval.com

Tel. 93 565 10 70
Fax. 93 575 39 45

ANDALUCIA Pol. Ind. Calonge C/ Automoción, 1 (Junto Peugeot), 41007, Sevilla andalucia@broncesval.com

Tel. 95 443 06 51
Fax. 95 443 04 29