Aluminium Alloy Magnesium Silicon 6063

  ALUMINUM ALLOY MAGNESIUM SILICON 6063

Products
Sheets - Plates - Bars - Tubes Profiles  Wire


Application and uses
Molds industry of the footwear.
Molds of bottles of plastic for blown.
Molds thermoformed.
Molds industry of the rubber.
Molds and counterfoils for the industry in general.
Models for the foundation and plates.

General use in machinery and industrial construction along with automation in industrial vehicles.


Thermal Treatments
Placed in solution: 520º C + - 5º C. from 0,5 to 1 hour.
Placed in cold water (40º C máx). As soon as possible.
Hardness: State T4, 8 days mínimum 20º C.
Artificial hardness: State T6, 8 hours at 175 ºC or 6 hours at 185º +-5º C.
Recooked: 1 to 2 hours at 380º - 420º C, following the cooling down process. Obtain peices Forged: 350º to 500º C.


Technological Aptitude
MB: very good
B: good
R: moderate
M: bad, avoid



Soldered
- On the fire .............................(B)
- Under argon gas .....................(B)
- Under electrical resistance.........(MB)
- Brass .....................................(MB)


Mechanization:
-Fragmentation of the chip....... State T5: (R)
-Surface shine.......................... Statet5: (MB)


Natural Composure
-In rural climate ..................(MB)
-In industrial climate ............(MB)
-In Sea climate....................(B)
-In salt water ......................(R)


Stamping:
-Expansion ..........................State T5 (M)
-Stamping deep............State T5 (R)


Anodized
-protection.................................(MB)
-Decorative ..............................(B)
-Anodized hardness.................(MB)


Bossage
-In state T5: .....................(R)

 

table
 
Chemcial Qualities
%
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
Otros
Al
Min.Max
0´30
0´60
0,10
0,30
0,10
0,30
0,40
0,60
0,05
0,15
0,20
0,15
Rest
                     

International Equivalencies
USA
SPAIN
FRANCE
GERMANY
G.B
SWEEDEN
SWITZERLAND
CANADA
ITALY
A.A.
 
U.N.E.
AFNOR
DIN(1712-1725)
B.S.
S.I.S.
VSM
ALCAN
UNI
6063
 
L-3441
38.337
A-GS
AIMg4SiO,5
3.3206
H9
4103
Extrudal
50 S
3569

Mechanical Properties
STATE
BREAKING POINT
Rm N/mm2
ELASTICITY LIMIT
Rp 0.2 N/mm2
STRECTHING
5,65 V So
RESISTANCE TO
Shear
N/mm2
HARDNESS
Brinell(HB)
Vickers
T4
150
90
22
-
42
-
T5
220
170
14
140
65
-

Physical Properties
ELASTIC MODULE
N/mm2
SPECIFIC WEIGHT
gms/cm3
TEMPERATURE OF FUSION
COEFFICIENT OF
DILATAC. LINEAR
(20º-100º) 10-6/ºC
THERMAL CONDUCTIVITY
w/m ºC
ELECTRICIAL RESISTANCE
Micro Ohm cm.
ELECTRICAL CONDUCTIVITY
% IACS
 
69.000
2,70
580-650
23´5
170
3´6
-
0´86

Radioes (radiuses) of Folded
STATE
COEF
0´4-0´8 m/m
0´8-1´6 m/m
1´6-3´2 m/m
3´2-4´8 m/m
4´8-6 m/m
6-10 m/m
10-12 m/m
T4
K
-
-
-
-
-
-
-
T5
K
-
-
-
-
-
-
-
-
K
-
-
-
-
-
-
-
 
 

Headquarters

VALENCIA Pol. Ind. Fuente del Jarro C/Ciudad de Elda, 17-19 46988, Paterna, Valencia broncesval@broncesval.com

Commercial Tel. 96 134 07 76
Fax. 96 134 09 43

Admin. Tel. 96 134 34 21
Fax.96 134 12 28

Delegations

CATALUNYA Pol. Ind. Molí dén Xec Can Barneda, 5  (Junto Baricentro), 08291, Ripollet catalunya@broncesval.com

Tel. 93 565 10 70
Fax. 93 575 39 45

ANDALUCIA Pol. Ind. Calonge C/ Automoción, 1 (Junto Peugeot), 41007, Sevilla andalucia@broncesval.com

Tel. 95 443 06 51
Fax. 95 443 04 29