Aluminium Alloy Magnesium Silicon 6061

  ALUMINUM ALLOY MAGNESIUM SILICON 6061

Products
Sheets - Plates - Bars - Tubes Perfiles  Wire


Application and uses

Molds industry of the footwear.
Molds of bottles of plastic for blown.
Molds thermoformed.
Molds industry of the rubber.
Molds and counterfoils for the industry in general.
Modls for the foundation and plates.

General use in machinery and industrial construction along with automation in industrial vehicles.


Thermal Treatments

Placed in solution: 535º C + - 5º C. from 0,5 to 2 hours.
Placed in cold water (40º C máx). As soon as possible.
Hardness: State T4, 8 days mínimum 20º C.
Artificial hardness: State T6, 8 hours at 175 ºC or 6 hours at 185º +-5º C.
Recooked: 30 min. at 2 hours at 380º - 420º C, following the cooling down process.Obtain peices Forged: 350º to 500º C.


Technological Aptitude

MB: very good
B: good
R: moderate
M: bad, avoid



Welding

On the fire ............................(MB)
Under argon gas.... ................(B)
Under electrical resistance........(B)
Brass......... ...........................(B)


Mechanization:

Fragmentation of thechip..... State 0: (M) State T6(R)
Surface sheen........................State 0: (R) State T6(MB)


Natural Composure

In rural climate ..................(MB)
In industrial climate ............(MB)
In Sea climate....................(B)
In salt water ......................(R)


Stamping:

Expansion ..........................State (MB) State H24 (M)
Stamping deep............State 0 (MB)State H24 (M)


Anodized

Protection..........................(MB)
Decorative ........................(R)
Anodized hard .................(MB)


Reputed

State0: ............................(T6)

 

table
 
Chemcial Qualities
%
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
Other
Al
Min.Max
0´40
0´68
0,70
0,15
0,40
0,15
0,80
1,20
0,04
0,35
0,25
0,15
0,15
Everything
                     

International Equivalencies
USA
SPAIN
FRANCE
GERMANY
G.B
SWEEDEN
SWITZERLAND
CANADA
ITALY
A.A.
 
U.N.E.
AFNOR
DIN(1712-1725)
B.S.
S.I.S.
VSM
ALCAN
UNI
6061
 
L-3420
38.342
A-SG
AIMg4SiCu,
3.3211
H20
 
Anticorodal-100
65 S
6170

Mechanical Properties
STATE
BREAKING POINT
Rm N/mm2
ELASTICITY LIMIT
Rp 0.2 N/mm2
STRECTHING
5,65 V So
RESISTANCE TO
SHEAR
N/mm2
HARDNESS
Brinell(HB)
Vickers
0
120
60
28
80
30
 
T4
230
130
23
160
65
69
T5
310
270
13
200
95
100

Physical Properties
ELASTIC MODULE
N/mm2
SPECIFIC WEIGHT
gms/cm3
TEMPERATURE OF FUSION
COEFFICIENT OF
DILATAC. LINEAR
(20º-100º) 10-6/ºC
69.500
2,70
580-650
23´5
THERMAL CONDUCTIVITY
w/m ºC
ELECTRICIAL RESISTANCE
Micro Ohm cm.
ELECTRICAL CONDUCTIVITY
% IACS
POTENTIAL OF DISSOLUTION
156
4´1
40´1
-0´83

Radioes (radiuses) of Folded
STATE
COEF
0´4-0´8 m/m
0´8-1´6 m/m
1´6-3´2 m/m
3´2-4´8 m/m
4´8-6 m/m
6-10 m/m
10-12 m/m
T4
K
-
-
-
-
-
-
-
T5
K
-
-
-
-
-
-
-
0
K
1´5
2´5
3´5
3´5
4
4´5
5
 
 

Headquarters

VALENCIA Pol. Ind. Fuente del Jarro C/Ciudad de Elda, 17-19 46988, Paterna, Valencia broncesval@broncesval.com

Commercial Tel. 96 134 07 76
Fax. 96 134 09 43

Admin. Tel. 96 134 34 21
Fax.96 134 12 28

Delegations

CATALUNYA Pol. Ind. Molí dén Xec Can Barneda, 5  (Junto Baricentro), 08291, Ripollet catalunya@broncesval.com

Tel. 93 565 10 70
Fax. 93 575 39 45

ANDALUCIA Pol. Ind. Calonge C/ Automoción, 1 (Junto Peugeot), 41007, Sevilla andalucia@broncesval.com

Tel. 95 443 06 51
Fax. 95 443 04 29