Aluminium Alloy Copper 2017

  ALUMINUM ALLOY COPPER 2017

 

Products
Bars, Plates, Sheets and Tubes

Aplication and uses
It is a question of an Alloy of high mechanical resistance obtained by structural hardening or treatment of putting in solution, temperature and ripeness.
It is applied in the industry of aviation, structural elements that need high mechanical characteristics, iron-works, screws, spikes. Clinches to be applied in condition(state) of temperature before the ripeness, molds of blown, worn, ultralight and wings delta.

Maintenance Temperature
Putting in solution: 500ºc + - 5ºc Temperature in cold water (40ºc máx.) natural ripeness: 4 days minimum to 20ºc Restew: 30 min. 2 hours to 375 º - 410ºc, followed(consecutive) by slow cooling.
For obtaining of wrought pieces: 380 to 480ºc.

Technological aptitudes

Welding

MB: Very Good
B: Good
R: Moderate
M: Bad

To the flame....................................(B)
To The low arch gas argon.................(M)
For electrical resistance.....................(MB)
Brassed...........................................(B)

Mecanization
Fragmentation of the chip.............State: T4 (B)
Surface Shine ...............................State: T4 (B)

Natural Composure
In rural environment ................(R)
In environment industry............(M)
In Marine environment..............(M)
In Salt Water environment........(M)

Anodized
In protection ........................(R)
Decorative ...........................(R)
Hard Anodized ....................(B)

Embossment

State: T4.....................(M)

Stamping

For expansion In State: T4 (M)
Deep stampingn In State: T4 (M)

     
Chemical Composition
%
Si
Fe
Cu
Mn
Mg
Cr
Zn
Ti
 
Otros
Al
Min.Max
0,20
0,80
0,70
3,50
4,50
0,40
1,00
0,40
1,00
0,10
0,25
 

Zr + Ti
0,25

0,15
Other


International Equivalencies
USA
SPAIN
FRANCE
GERMANY
G.B
SWEEDEN
SWITZERLAND
CANADA
ITALY
A.A.
 
U.N.E.
AFNOR
DIN(1712-1725)
B.S.
S.I.S.
VSM
ALCAN
UNI
2017
 
L-3120
38.312
A-U4G
AlCuMg1 3.1325
H14
 
Avional-100
17 S
3579


Mechanical Properties
State
Breaking Load
Rm N/mm2
Elasticity Limit
Rp 0.2 N/mm2
Length
5,65 V So
Resistence to
Shear
N/mm2
Life Span
Brinell(HB)
Vickers
0
200
100
20
260
45
 
T4
390
245
14
 
105
 


Physical Properties
Elastic Number
N/mm2
Specific Weight
gms/cm3
Temperature of fusión
ºC
Coefficient of
dilatac. linear
(20º-100º) 10-6/ºC
Thermal conductivity
w/m ºC
Electrical Resistance
Micro Ohm cm.
Conduct. electrical
% IACS
Potential to Dilute
V.
74.000
2,70
510-640
23,0
T4-134

5´1

-
0´69


Radioes (radiuses) of Folded
State
COEF
0,4-0,8 m/m
0,8-1,6 m/m
1,6-3,2 m/m
3,2-4,8 m/m
4,8-6 m/m
6-10 m/m
10-12 m/m
0
K
0
0
0´75
1
1´5
2´5
4
T4
K
2´5
3
4
5
5
6
 
 
K
     

 

 

   


To calculate the minimum radius, you must multiply the peice of metal by the coefficient of K.

Headquarters

VALENCIA Pol. Ind. Fuente del Jarro C/Ciudad de Elda, 17-19 46988, Paterna, Valencia broncesval@broncesval.com

Commercial Tel. 96 134 07 76
Fax. 96 134 09 43

Admin. Tel. 96 134 34 21
Fax.96 134 12 28

Delegations

CATALUNYA Pol. Ind. Molí dén Xec Can Barneda, 5  (Junto Baricentro), 08291, Ripollet catalunya@broncesval.com

Tel. 93 565 10 70
Fax. 93 575 39 45

ANDALUCIA Pol. Ind. Calonge C/ Automoción, 1 (Junto Peugeot), 41007, Sevilla andalucia@broncesval.com

Tel. 95 443 06 51
Fax. 95 443 04 29